Dielectric relaxation and modulus studies of PEO-PAM blend based sodium salt electrolyte system
Publication details: New Delhi NISCAIR 2018Edition: Vol. 56(12), DecemberDescription: 978-988Subject(s): Online resources: In: Indian journal of pure & applied physics (IJPAP)Summary: Dielectric properties of solid polymer electrolyte having PEO-PAM blend matrix with sodium trifluoromethane sulfonate (NaCF3SO3) as ionic salt have been studied. The samples have been prepared by solution cast technique. X-ray diffraction analysis has been carried to understand the formation of blend, complexation and crystallinity of the polymer blend with the variation of salt amount. Complex impedance spectroscopy has been used to study ionic conductivity, dielectric relaxation and modulus formalism as a function of frequency at various temperatures. Scaling of M" spectra has been carried out and it has been found that the dynamic relaxation processes occurring in the system are dependent on temperature as well as salt concentration. Highest conductivity at room temperature has been found to be 2.81x10-7 S/cm for sample with 17.5 wt% NaCF3SO3.| Item type | Current library | Status | Barcode | |
|---|---|---|---|---|
Articles Abstract Database
|
School of Pharmacy Archieval Section | Not for loan | 2018463 |
Dielectric properties of solid polymer electrolyte having PEO-PAM blend matrix with sodium trifluoromethane sulfonate (NaCF3SO3) as ionic salt have been studied. The samples have been prepared by solution cast technique. X-ray diffraction analysis has been carried to understand the formation of blend, complexation and crystallinity of the polymer blend with the variation of salt amount. Complex impedance spectroscopy has been used to study ionic conductivity, dielectric relaxation and modulus formalism as a function of frequency at various temperatures. Scaling of M" spectra has been carried out and it has been found that the dynamic relaxation processes occurring in the system are dependent on temperature as well as salt concentration. Highest conductivity at room temperature has been found to be 2.81x10-7 S/cm for sample with 17.5 wt% NaCF3SO3.
There are no comments on this title.